    Sterilized chicken feather as eco-friendly corrosion inhibitor for mild steel in a water-based drilling mud–gravimetric and FTIR assessment
    (Sciencedomain International, 2024) Akintola, S.A.; Aleem, A.A.; Oki, M.; Ikubanni, P.P.; Adediran, A.A.; Esabunor, O.R.
    This research evaluated the corrosion performance of mild steel in sterilized and unsterilized alkaline mud corroding systems using chicken feather powder (CFP) obtained through the usual hydrolysis and acid neutralization protocol. Insightfully, gravimetric analysis revealed that bacterial infestation of the unsterilized environment caused its corrosion performance to be lower at 10.3% while the sterilized counterpart stood at 49% at 92 days of exposure to the environments respectively. The functional groups, C=N, O=C=O, H-C=O etc, revealed by FTIR to be present in the protein saturated feather were overwhelmed by microbial activities rendering them inactive to perform as inhibitors.
  • Thumbnail Image
    Item
    Valorized rice husk as green corrosion inhibitor for Al 6061 in 1M HCl
    (MIM Research Group, 2024) Ikubanni, P.; Oki, M.; Adediran, A.; Akintola, S.A.; Adeleke, A.; Anyim, I.; Adesina, O.; Efenovwe, L.
    This study investigated the inhibition characteristics of rice husk (RH) on corrosion of Aluminum 6061 in 1M hydrochloric acid. Gravimetric analysis and Scanning Electron Microscopy (SEM)/ Energy Dispersive X-ray analysis (EDX) as well as electrochemical studies revealed the potency of RH as a good inhibitor of the corrosion of Al 6061 in 1M HCl. Fourier Transform Infrared Spectroscopy (FTIR) indicated that –OH, C=C, and C=O with signals at (3317.19, 2932.9, 2848.2), (1631.8) and (1105.73, 1030.2, 447.15), respectively in RH were the viable active functional groups which adsorbed on the metal surface to effect reduction of corrosion rates. However, literature suggested the presence of amorphous silica in RH which served as a complimentary corrosion inhibitor. The corrosion current density of Al 6061 was reduced to 3.46 × 10−7 A/cm2 at 24 h as against 9.27 × 10−7 A/cm2 at the commencement of the potentiodynamic polarization measurements in inhibited 1M HCl. The control specimens exhibited an average corrosion rate of 3.86 × 10−6 A/cm2 in HCl solution at the start of this investigation as compared to the corrosion rate of 3.46 × 10−7 A/cm2 at 24 h of exposure in 5 mg RH- inhibited HCl. The obtained results gave a corrosion inhibition efficiency of about 90 to 92%.